Effect of Co doping on structural and mechanical properties of CeO2

Abstract

Sol-gel synthesized nanocrystalline Co doped CeO2 powders [(Ce1-xCoxO2; x=0, 0.03)] were made into cylindrical discs by uniaxial pressing and sintered at 1500°C for 24h to measure mechanical properties. The pure phase formation of undoped and Co doped samples were confirmed by X-ray diffraction and Raman analysis. The scanning electron microscopy (SEM) was used for observing the microstructure of sintered samples to investigate density, porosity, and grain size. The grains size observed for 1500°C sintered samples 5-8 μm. Vickers indentation method used for investigating the micro-hardness. For undoped CeO2 micro-hardness was found 6.2 GPa which decreased with Co doping. It was found that samples follow indentation size effect (ISE) and follow elastic than plastic deformation. Enhanced ductile nature with Co doping in CeO2 made it more promising material for optoelectronic device applications. © 2018 Author(s).